CYC S-Glass Roving for High Strength Composites

S-Glass Roving (High Strength Glass Fiber)

CYC S-glass roving (HS2, HS4, HS6) is made from magnesium-alumina-silicate glass system. Foreign countries named as R-glass or T-glass. Due to its high tensile strength, high tensile modulus, excellent impact resistance, aging & corrosion resistance properties, they are widely used in high performance composites industries, such as military, aerospace, weapons, marine & shipbuilding, civil industry, sports and recreation industry.

PRODUCT FEATURES:
High tensile strength
High tensile modulus
Compatible with Epoxy, Phenolic & Vinly ester resin
Excellent aging & corrosion resistance

 

S-GLASS FIBER PROPERTIES:

Physics Properties

HS2 HS4 HS6
Original Fiber Tensile Strength (MPa) ≥4100 (590KSI) ≥4600 (660KSI) ≥4800 (690KSI)
Epoxy Wet Fiber Tensile Strength (MPa) 3000~3400 (435~490KSI) 3200~3600 (460~520KSI) 3600~4000 (520~580KSI)
Tensile Modulus (GPa) 87~91 90~94 92~96
Elongation at Break (%) 5.3 5.3 5.7
Softening Point (℃) 910 940 960

 

TYPICAL PRODUCT SPECIFICATIONS:

Product Code Filament Diameter (μm) Linear Density (tex)

Tensile Strength

(MPa)

Moisture Content (%) Loss On Ignition (%) Compatible Resin
SCY11-HS2-240 11 240 ≥3000 ≤0.20 0.50~1.10 EP/VE/PE
SCY11-HS4-240 11 240 ≥3200 ≤0.20 0.50~1.10
SCY11-HS6-240 11 240 ≥3600 ≤0.20 0.50~1.10
SCY11-HS2-660 11 660 ≥3000 ≤0.20 0.50~1.10
SCY11-HS4-660 11 660 ≥3200 ≤0.20 0.50~1.10
SCY11-HS6-660 11 660 ≥3600 ≤0.20 0.50~1.10
SCY17-HS2-2400 17 2400 ≥3000 ≤0.20 0.50~1.10

Notes: Customized specification is available.

 

PACKAGING:

The roving bobbins/spools packing by standard exporting carbon box or pallets.

 

STORAGE:

Unless otherwise specified, the roving should be stacked in dry and cool place, do not open the package cause damp.